Default Unbalanced skins on sandwich construction

Hi all,

Soon I will make my first by piece carbon fiber / foam(infusion), I've been reading and I've read that carbon when is loaded in compression, show properties very different that loading in tension. Tensile strength compared with compressive strength can be half , module however does not seem to change much. Then, if I know which side will be compressed:
Should I apply more layers over skin that is compressed for better weight / resistance?


Regards and thanks
compoforo is offline   Reply With Quote
Reply

Bookmarks

Tags
construction, sandwich, skins, unbalanced

Thread Tools
Display Modes

Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is Off

Forum Jump


All times are GMT -8. The time now is 07:29 PM.
Powered by vBulletin® Version 3.8.7
Copyright ©2000 - 2017, vBulletin Solutions, Inc.

Inactive Reminders By Icora Web Design